Cu-Ag-Rear Metals for Wires: Processing and Characterisation
Keywords:
Cu based alloy, arc-melting, mechanical alloying, microstructure, microhardness
Abstract
Cu based alloy microalloyed with rear metals (RM) (in our case, sample with Nb) for wires were prepared by two different techniques arc-melting and mechanical alloying. Microstructure characterisation was carried out by SEM including EDX and X-ray measurements. Mechanical measurements at room temperature were performed and the results of materials obtained by different techniques are analised.
Nanocristaline microstructure it was observed and this is associated with fine graine refinament of CuAgRM material after both technologies.
Downloads
Download data is not yet available.
References
[1]. V.I. Pantsyrnyi, A.K. Shikov, A.D. Nikulin, A.E. Vorobova, E.A. Dergunova, A.G. Silaev, N.A. Bel’akov, I.I. Potapenko, IEEE Trans. Magn. 32 (4) (1996) 2866.
[2]. A. Inoue, T. Zhang, A. Takeuchi: Appl. Phys. Lett. 71 (1997) 464.
[3]. E. Botcharova, J. Freudenberger, A. Gaganov, Materials Science and Engineering A 416 (2006) 261–268.
[4]. X.H. Lin, W.L. Johnson, W.K. Rhim: Mater. Trans. JIM 38 (1997) 5.
[5]. A. Gebert, J. Eckert, L. Schultz: Acta Mater. 46 (1998) 5.
[6]. K. Werniewicz, U.Kuhn, N. Mattern, B. Bartusch, J. Eckert, J. Das, L. Schultz, T. Kulik: Acta. Mater. 55 3513 (2007).
[7]. S. Ichikawa, K. Miyazawa, H. Ichinose, K. Ito, Nanostruct. Mater. 11(1999) 1301.
[8]. E.Bocharova, Ph.D. Thesis, TU Dresden, Germany, www.ifwdresden.de/imw/theses/Dr Bocharova.pdf.
[2]. A. Inoue, T. Zhang, A. Takeuchi: Appl. Phys. Lett. 71 (1997) 464.
[3]. E. Botcharova, J. Freudenberger, A. Gaganov, Materials Science and Engineering A 416 (2006) 261–268.
[4]. X.H. Lin, W.L. Johnson, W.K. Rhim: Mater. Trans. JIM 38 (1997) 5.
[5]. A. Gebert, J. Eckert, L. Schultz: Acta Mater. 46 (1998) 5.
[6]. K. Werniewicz, U.Kuhn, N. Mattern, B. Bartusch, J. Eckert, J. Das, L. Schultz, T. Kulik: Acta. Mater. 55 3513 (2007).
[7]. S. Ichikawa, K. Miyazawa, H. Ichinose, K. Ito, Nanostruct. Mater. 11(1999) 1301.
[8]. E.Bocharova, Ph.D. Thesis, TU Dresden, Germany, www.ifwdresden.de/imw/theses/Dr Bocharova.pdf.
Published
2011-06-15
How to Cite
1.
IORDACHE C, STOICA M, MOHSEN S, VLAD M. Cu-Ag-Rear Metals for Wires: Processing and Characterisation. The Annals of “Dunarea de Jos” University of Galati. Fascicle IX, Metallurgy and Materials Science [Internet]. 15Jun.2011 [cited 23Dec.2024];34(2):33-7. Available from: https://gup.ugal.ro/ugaljournals/index.php/mms/article/view/2950
Issue
Section
Articles