TRIBOLOGICAL EVALUATION OF SOYBEAN OIL ADDITIVATED WITH NANO GRAPHENE
Résumé
This paper presents the influence of adding nano graphene particles in soybean oil in different massic concentration (0.25%, 0.50% and 1%) on the tribological parameters: friction coefficient, wear scar diameter. Tests are done on a four-ball machine from the lubricant laboratory LubriTest, at “Dunarea de Jos” University of Galati. The test parameters were load: 100 N, 200 N and 300 N and the speed 1800 rpm. The additive was supplied by PlasmaChem and the dry graphene - nanoplatelets have a thickness: 1-4 nm; particles size: up to 2 µm, purity: 91 at.%. The soybean oil was supplied by Prutul Galati. The test balls are lime polished, made of chrome alloyed steel balls, having 12.7±0.0005 mm in diameter, with 64-66 HRC hardness, as delivered by SKF. The sample oil volume required for each test was 8 ml ±1 ml. The test method for investigating the lubricating capacity was EN ISO 20623:2003 Petroleum and related products - Determination of the extreme-pressure and anti-wear properties of fluids - four ball method.
All rights are reserved for this publication, which is copyright according to the Romanian law of copyright. Excepting only any fair dealing for the purpose of the private study, research, review, comment and criticism, no part of this publication may be reproduced, stored in a retrieval system or transmitted in any form or by any means, mechanical, electrical, electronic, optical, photocopying, recording or otherwise, without the prior express permission of the copyright owners.