Researches Regarding Structural Changes due to nickel Microlalloying of Hot Galvanizing Baths
Abstract
This work offers a synthesis of researches performed in laboratory and regards the nickel microalloying of hot galvanizing baths. Experiments followed the structural changes of both hot galvanizing bath and deposed layer with effect on layer properties.
Characterization of deposed layer and nickel microalloying of galvanizing bath performed by spectral chemical analysis, optical microscopy and X ray diffraction emphasized the structural constituents nature as well as changes shown up depending on nickel concentration of galvanizing bath. Correlation diagrams between deposed layer thickness and structural constituents were also made.
Experimental results emphasized a close interdependence between nickel concentration and microstructure. This allowed to settle the optimal nickel concentration required by galvanizing bath microalloying with maximum effect upon hot galvanizing coating properties.
Downloads
References
[2]. G. P. Lewis, J. Pederson - Optimizing the Ni-Zn process for hot dip galvanizing, Cominco LTD., 1998.
[3]. C. Alonso, J. Sanchez, J. Fullea, C. Andrade, P. Tierra, M. Bernal - The addition of nickel to improve the corrosion resistance of galvanized reinforcement, 1995.
[4]. D. Stroud - Galvanizing with Zn-Ni alloy, Proceedings first Asian-Pacific General Galvanizing Conference, Taiwan, 1992.